Bars, wire, forgings, flash welded rings, and extrusions shall be solution heat treated in accordance with AMS-H-6875 by. heating to 1900 °F ± 25 °F (1038 °C ± 14 °C), holding at heat for a time commensurate with section thickness, heating. equipment, and procedure used, and cooling as required to below 90 °F (32 °C).
AMS 5643 (also known as 17-4 PH Stainless Steel) is a high-strength, high-temperature Stainless Steel alloy widely used in aerospace, chemical, and petrochemical industries. The AMS 5643 provides outstanding strength and excellent performance in high-temperature conditions. This alloy is a versatile material that can be cold-worked to …
Hot compression tests were performed on the samples of AMS 5643 stainless steel in the temperature range of 900–1050 °C and at strain rates of 10−3–1 s−1. Single peak stress flow behavior was observed at all deformation situations. The flow curves were characterized by a faint peak and slight flow softening which suggested continuous …
0.15 - 0.45. 3.0 - 5.0. 17-4 PH is a martensitic, precipitation-hardening stainless steel that provides an outstanding combination of high strength and hardness along with excellent corrosion resistance. 17-4 PH has good fabricating characteristics and can be age hardened by a single step, low temperature treatment. 17-4 PH is a versatile