AMS 5643 (also known as 17-4 PH Stainless Steel) is a high-strength, high-temperature Stainless Steel alloy widely used in aerospace, chemical, and petrochemical industries. The AMS 5643 provides outstanding strength and excellent performance in high-temperature conditions. This alloy is a versatile material that can be cold-worked to …
Details. This grade of stainless steel has a typical density of 7.75kg/dm³ and can be magnetised. 17 4PH finds specific use in applications where a combination of unusually high strength and moderate corrosion resistance is a determining factor. The alloy has similar corrosion resistance characteristics when compared to 304 stainless steel.
0.15 - 0.45. 3.0 - 5.0. 17-4 PH is a martensitic, precipitation-hardening stainless steel that provides an outstanding combination of high strength and hardness along with excellent corrosion resistance. 17-4 PH has good fabricating characteristics and can be age hardened by a single step, low temperature treatment. 17-4 PH is a versatile
Hot compression tests were performed on the samples of AMS 5643 stainless steel in the temperature range of 900–1050 °C and at strain rates of 10−3–1 s−1. Single peak stress flow behavior was observed at all deformation situations. The flow curves were characterized by a faint peak and slight flow softening which suggested continuous …
3.3 Heat Treatment: Bars, wire, forgings, mechanical tubing, and flash welded rings shall be solution heat treated to. 1900 °F ± 25 (1038 °C ± 14), holding at heat for a time commensurate with section thickness, heating equipment, and procedure used, and cooling as required to below 90 °F (32 °C). -3-.
AMS 5643. Stainless Steel Grade: 17-4 PH. Product Forms: Steel, Bars and Forgings, Corrosion Resistant. Condition: Precipitation Hardening. Product availability: Stainless Steel Grade 17-4 PH Round Bar. DISCLAIMER: The use of this information should be considered strictly voluntary. Information contained in this page or across the domain, may
AMS 5643 AMS 5643 H1150 AMS 5604 ASTM A564 TYPE 630. 17-4 Stainless is a martensitic chromium-nickel-copper stainless steel in the solution treated (annealed) condition. It can be further hardened to various strength levels by a single precipitation hardening heat treatment that minimizes scaling and distortion. Its strength and moderate