Usually, ASTM A249 tubing sizes and wall thickness separately are 1/8 in (3.2 mm) in inside diameter to 12 in (304.8 mm) in outside diameter and 0.015 in to 0.32 in (0.4 – 8.1 mm). The tubing sizes and thicknesses furnished to ASTM A269 are 1/4 in. (6.4 mm) in inside diameter and larger and 0.020 in. (0.51 mm) in nominal wall-thickness and
ASTM A269 tubes should be welded type or seamless type, which is made in cold finished or hot finished. Testing And Quality Control Tube Surface. Both ASTM A249 and ASTM A269 specifications, after heat treatment, tubes should be pickled free of scale, when bright annealing is used, pickling is not necessary. Heat Treatment
Designation: A269/A269M − 15aStandard Specif i cation forSeamless and Welded Austenitic Stainless Steel Tubing forGeneral Service 1This standard is issued under the f i xed designation A269/A269M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision.
ASTM A269/A269M-15a(2019) en-US Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service Standard A269/A269M Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing for General Service> new BOS Vol. 01.01 Committee A01
Current edition approved March 1, 2008. Published April 2008. Originally approved in 1944. Last previous edition approved in 2007 as A 269 – 07a. 2 For referenced ASTM standards, visit the ASTM website,, or contact ASTM Customer Service at [email protected]. For Annual Book of ASTM Standards volume information, refer to the
Common stainless steel grades of ASTM A269. ASTM A269 TP304; ASTM A269 TP304L; ASTM A269 TP316; ASTM A269 TP316L; Sizes And Dimension. Usually, ASTM A249 tubing sizes and wall thickness separately are 1/8 in (3.2 mm) in inside diameter to 12 in (304.8 mm) in outside diameter and 0.015 in to 0.32 in (0.4 – 8.1 mm).
The ASTM A269 tubing refers to series of seamless or welded austenitic stainless steel tubing for general corrosion-resisting and low- or high-temperature service. TP304, TP304L, TP316 and TP316L are the most widely used grades and are often found available in stock. Sizes & dimensions, characteristics & applications, chemical …
Abstract. This specification covers nominal-wall-thickness, seamless and welded austenitic steel tubing for general corrosion-resisting and low- or high-temperature service. All material shall be furnished in the heat-treated condition. The steel shall conform to the chemical composition requirements. Different mechanical test requirements that
ASTM A269 tp304 grade is designed with a chemical content containing 18% chromium and 8% nickel. The ASTM A 269 tp316 grade is made up of a chemical concentration of 16% chromium 10% nickel, with 2% molybdenum. The SS 316 grade has higher corrosion and pitting resistance when compared to standard 304 stainless steel …